Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
Comparative Study
. 1999 Mar 15;44(4):446-55.
doi: 10.1002/(sici)1097-4636(19990315)44:4<446::aid-jbm11>3.0.co;2-f.

Poly(alpha-hydroxyl acids)/hydroxyapatite porous composites for bone-tissue engineering. I. Preparation and morphology

Affiliations
Free article
Comparative Study

Poly(alpha-hydroxyl acids)/hydroxyapatite porous composites for bone-tissue engineering. I. Preparation and morphology

R Zhang et al. J Biomed Mater Res. .
Free article

Abstract

Tissue engineering has shown great promise for creating biological alternatives for implants. In this approach, scaffolding plays a pivotal role. Hydroxyapatite mimics the natural bone mineral and has shown good bone-bonding properties. This paper describes the preparation and morphologies of three-dimensional porous composites from poly(L-lactic acid) (PLLA) or poly(D,L-lactic acid-co-glycolic acid) (PLGA) solution and hydroxyapatite (HAP). A thermally induced phase separation technique was used to create the highly porous composite scaffolds for bone-tissue engineering. Freeze drying of the phase-separated polymer/HAP/solvent mixtures produced hard and tough foams with a co-continuous structure of interconnected pores and a polymer/HAP composite skeleton. The microstructure of the pores and the walls was controlled by varying the polymer concentration, HAP content, quenching temperature, polymer, and solvent utilized. The porosity increased with decreasing polymer concentration and HAP content. Foams with porosity as high as 95% were achieved. Pore sizes ranging from several microns to a few hundred microns were obtained. The composite foams showed a significant improvement in mechanical properties over pure polymer foams. They are promising scaffolds for bone-tissue engineering.