Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 1999 Mar;15(2):87-97.
doi: 10.1016/s0109-5641(99)00018-4.

The influence of clinically induced variability on the distribution of compressive fracture strengths of a hand-mixed zinc phosphate dental cement

Affiliations

The influence of clinically induced variability on the distribution of compressive fracture strengths of a hand-mixed zinc phosphate dental cement

G J Fleming et al. Dent Mater. 1999 Mar.

Abstract

Objectives: Conventional approaches to comparing dental cements use standard property tests under manufacturers' specified conditions. Zinc phosphate cements are supplied in powder/liquid form and manipulation frequently involves mixing the components by eye so a range of mixing ratios will inevitably occur in practice. Unfortunately, the physical, chemical, biological and mechanical properties of cements are known to be dependent on the mixing ratio.

Methods: Forty dental nurses prepared a series of three cement samples to a luting consistency they considered acceptable for use in practice.

Results: It was found that each dental nurse produced consistent cement mixes, although, the mixing ratios varied from 1.7 to 3.2 g/ml between nurses. The mean compressive strength, standard deviation and associated Weibull Moduli (m) of the cements were determined as a function of this mixing ratio range and showed considerable variation ranging from 33.5 +/- 3.2 MPa (m = 11.0) at 1.7 g/ml to 71.4 +/- 8.4 MPa (m = 8.6) at 2.6 g/ml and 42.5 +/- 10.0 MPa (m = 5.0) at 3.2 g/ml.

Significance: An analytical approach was adopted which facilitated an integrated analysis of the mixing ratio variability with the strength data. It was found for the test group of dental nurses that 25% of cement mixes produced would have achieved strengths below 40 MPa whilst strengths below the standard value were produced in at least 70% of mixes. These results indicate that a simple analysis of the properties of cements manipulated under optimum conditions, provides little information on the material characteristics obtained in practice because of clinically induced variability.