Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2001 Aug;22(15):2171-5.
doi: 10.1016/s0142-9612(00)00408-7.

Influence of thickness on the properties of hydroxyapatite coatings deposited by KrF laser ablation

Affiliations

Influence of thickness on the properties of hydroxyapatite coatings deposited by KrF laser ablation

J M Fernandez-Pradas et al. Biomaterials. 2001 Aug.

Abstract

The growth of hydroxyapatite coatings obtained by KrF excimer laser ablation and their adhesion to a titanium alloy substrate were studied by producing coatings with thicknesses ranging from 170 nm up to 1.5 microm, as a result of different deposition times. The morphology of the coatings consists of grain-like particles and also droplets. During growth the grain-like particles grow in size, partially masking the droplets, and a columnar structure is developed. The thinnest film is mainly composed of amorphous calcium phosphate. The coating 350nm thick already contains hydroxyapatite, whereas thicker coatings present some alpha tricalcium phosphate in addition to hydroxyapatite. The resulting coating to substrate adhesion was evaluated through the scratch test technique. Coatings fail under the scratch test by spallating laterally from the diamond tip and the failure load increases as thickness decreases, until not adhesive but cohesive failure for the thinnest coating is observed.