Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2003 Sep;24(21):3787-94.
doi: 10.1016/s0142-9612(03)00260-6.

Toughness, bonding and fluoride-release properties of hydroxyapatite-added glass ionomer cement

Affiliations

Toughness, bonding and fluoride-release properties of hydroxyapatite-added glass ionomer cement

Milanita E Lucas et al. Biomaterials. 2003 Sep.

Abstract

Improving the mechanical strength of glass ionomer cement while preserving its favorable clinical properties such as fluoride release, bonding to tooth structure and biocompatibility is desirable. In this study, hydroxyapatite was incorporated into chemically setting glass ionomer cement and its effect on the fracture toughness, bonding to dentin and fluoride release was identified. Commercial glass ionomer cement (Fuji IX GP((R)) ) was the control and base material. Eight weight percent of hydroxyapatite was added into the glass ionomer powder. Specimens were fabricated and the fracture toughness, shear bond strength and eluted fluoride ion concentration were measured. Adding hydroxyapatite into the glass ionomer cement led to significantly higher fracture toughness after 15min and 24h from mixing. The hydroxyapatite-added cement also exhibited bond strength to dentin similar to that of the control from 15min to 56 days and consistent fluoride release for 13 weeks. SEM findings showed a cohesive type of fracture in the material for all specimens in both groups. These results indicate that hydroxyapatite-added glass ionomer cement has a potential as a reliable restorative material with improved fracture toughness, long-term bonding to dentin and unimpeded ability of sustained fluoride release.