Shear bond strengths and microleakage of four types of dentin adhesive materials

Abstract

The aim of this investigation was to compare the microleakage of composite resin (Z-100) and shear bond strength to bovine dentin using different types of adhesive systems (Scotch Bond Multi-Purpose, All-Bond 2, One-Step, and Perma Quick) to compare and correlate microleakage to shear bond strength. For the microleakage aspect of the study, 20 class V were prepared (bovine incisors) with 90-degree cavosurface margins and were located at the cemento-enamel junction using a template. Each dentin bonding system was applied to five cavities following the manufacturer's instructions and restored with Z-100 composite resin. After 24 hours of storage in distilled water at 37 degrees C, the teeth were immersed in 2% basic fuchsin dye. All teeth were sectioned in a mesiodistal direction using a diamond saw, and each section was then inspected under a stereomacroscope. For the shear bond strength aspect of the study, 20 bovine incisors were centrally horizontally mounted in Teflon mold with cold cure acrylic resin. Flat labial dentin surfaces were prepared using different grit silicon carbide abrasive wheels. Five specimens were used for each of the bonding agent systems. Each specimen was bonded with restorative composite resin (Z-100) and applied to the treated dentinal surface through a split Teflon mold. All specimens were stored in distilled water at 37 degrees C for 24 hours. The bonds were stressed using shear forces at a crosshead speed of 0.5mm/min using an Instron Universal testing machine. Findings indicate none of the systems tested in this study were free from microleakage. Scotch bond multi-purpose achieved the best seal, with One-Step being second best, while All-Bond 2 and Perma Quick had the poorest seal. However, there were significant differences among the shear bond strengths of the four bonding systems tested. Scotch Bond Multi-Purpose has a higher bond strength to composite resin when compared to the other dentin adhesives. The study also concluded there is no association between microleakage and shear bond strength.