Early pattern of calcification in the dorsal carapace of the blue crab, Callinectes sapidus

Abstract

The pattern of calcium carbonate deposition was observed in the dorsal carapace of premolt (D2-D3) and early postmolt (0-48 h) blue crabs, Callinectes sapidus, using scanning (SEM) and transmission (TEM) electron microscopy. Samples of dorsal carapace for SEM were quick-frozen in liquid nitrogen, subsequently lyophilized, and viewed using secondary and backscattered electrons as well as X-ray maps of calcium. Pieces of lyophilized cuticle were also embedded in epoxy resin and subsequently sectioned and viewed with TEM and SEM. Fresh pieces of dorsal carapace for TEM were also fixed in 2.5% glutaraldehyde in phosphate buffer followed by postfixation in 1% OsO4 in cacodylate buffer. Calcium concentrations were determined using atomic absorption spectrophotometry and quantitative X-ray microanalysis. Calcium accumulation began in the cuticle at 3 h postmolt at the epicuticle/exocuticle boundary and at the distal and proximal margins of the interprismatic septa (IPS). The bidirectional calcification of the IPS continued until the two fronts met at 5-8 h postmolt. The roughly hexagonal walls of the IPS formed a honeycomb-like structure that resulted in a rigid cuticle. The walls of the canal containing sensory neurons also calcified at 3 h, thereby imparting rigidity to the structure and additional strength to the cuticle. Examination of thin sections of lyophilized cuticle and fixed cuticle revealed that the first mineral deposited is more soluble than calcite and is probably amorphous calcium carbonate. The amorphous calcium carbonate is transformed to calcite along a front that follows the original deposition and is probably controlled by a specialized matrix within the IPS. Since amorphous calcium carbonate is isotropic, it would also make the mineral in the exocuticle stronger by an equal distribution of mechanical stress.