[Effect of saliva contamination on microleakage around class-5 cavities restored with three different types of adhesive materials]

Abstract

The recent improvement of adhesive materials should decrease the risk related to saliva contamination. The aim of this study was to evaluate the effect of saliva contamination on the microleakage within class V cavities restored with three different types of materials: conventional glass ionomer cement, composite resin and compomer. 30 human extracted teeth were randomly divided in 3 equal groups. In each group, class V cavities were prepared on both facial and lingual surfaces (but joint for glass ionomer cement and bevelled incisal margin for composite resin and compomer). The lingual cavities were contaminated with saliva prior to restoration, while the facial cavities were not contaminated, serving as control. After water storage for 24 hours, teeth were immersed in 1% methylene blue solution for 24 hours. The axial sections were viewed under an optical microscope and the extent of dye penetration along cervical, axial and incisal margins was measured in millimetres. Statistic analysis showed that under salivary contamination, microleakage increased along the cervical margin of restoration for all three tested materials. Saliva contamination resulted in microleakage within the axial wall of the cavity only for the conventional glass ionomer cement. These data indicate that composite resin and compomer used together with new adhesives seem to be less sensitive to saliva contamination compared to conventional materials. However, under saliva contamination, cervical microleakage cannot be completely prevented and proper isolation should still be mandatory.