[Preparation and characterization of Mn-Zn ferrite oxygene nanoparticle for tumor thermotherapy]

Abstract

With the sulfate as the materials and NaOH as precipitator, Mn(0.4)Zn(0.6)Fe2O4 nanoparticles were produced, which are proved to be spinel Mn-Zn ferrite analyzed by X-ray diffraction(XRD). Their shapes are approximately global examined by transmission electron microscopy(TEM) and their average diameter is 50 nm measured with image analysis-system. The Curie temperature was measured and in vitro heating test in a alternating magnetic field was carried out. The results show that the Curie temperature is 105. 407 degrees C, While its magnetic fluid could rise to 43 degrees C - 47 degrees C due to different concentration in a alternating magnetic field. The result provide theoretical and practical evidence to select an appropriate material and concentration for tumor