Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2009 Sep 30;131(38):13833-9.
doi: 10.1021/ja905467v.

Layered double hydroxides as highly efficient photocatalysts for visible light oxygen generation from water

Affiliations

Layered double hydroxides as highly efficient photocatalysts for visible light oxygen generation from water

Cláudia Gomes Silva et al. J Am Chem Soc. .

Abstract

Oxygen generation through photocatalytic water splitting under visible light irradiation is a challenging process. In this work we have synthesized a series of Zn/Ti, Zn/Ce, and Zn/Cr layered double hydroxides (LDH) at different Zn/metal atomic ratio (from 4:2 to 4:0.25) and tested them for the visible light photocatalytic oxygen generation. The most active material was found to be (Zn/Cr)LDH with an atomic ratio of 4:2 that exhibits two absorption bands in the visible region at lambda(max) of 410 and 570 nm. It was found that the efficiency of these chromium layered double oxides for oxygen generation increases asymptotically with the Cr content. Using iron oxalate as chemical actinometer we have determined that the apparent quantum yields for oxygen generation (Phi apparent = 4 x mol oxygen/mol incident photons) are of 60.9% and 12.2% at 410 and 570 nm, respectively. These quantum yields are among the highest values ever determined with visible light for solid materials in the absence of light harvesting dye. The overall efficiency of (Zn/Cr)LDH for visible light oxygen generation was found to be 1.6 times higher than that of WO(3) under the same conditions.