Characterization of a new photorefractive material: K(l-y)L(y)T(1-x)N(x)

Abstract

We report the growth and characterization of a new photorefractive material, potassium lithium tantalate niobate (KLTN). A KLTN crystal doped with copper is demonstrated to yield high diffraction efficiency of photorefractive gratings in the paraelectric phase. Voltage-controllable index gratings with n(1) = 8.5 x 10(-5) were achieved, which yielded diffraction efficiencies of 75% in a 2.9-mm-thick sample. In addition, diffraction was observed in the paraelectric phase without an applied field. This effect is attributed to a growth-induced strain field.