Effects of metal primers on bonding of adhesive resin cement to noble alloys for porcelain fusing

Abstract

This study evaluated the effects of metal primers on the bonding of adhesive resin to four pure metals (Au, Pd, Ag, Cu) and two noble alloys for porcelain fusing (high-gold and high-palladium content alloys). Bonding surface was polished with 600-grit silicon carbide paper and primed with one of the three metal primers (V-Primer, Metaltite, and M.L. Primer). Bonded specimens were fabricated by applying adhesive resin (Super-Bond C&B) on the primed surface. Shear bond strength (SBS) was determined both before and after thermocycling (4-60 degrees C for 2,000 cycles). The highest SBS values to each pure metal after thermocycling were 33.5 MPa for Au by M.L. Primer, 35.0 MPa for Ag by V-Primer, and 34.4 MPa for Cu by Metaltite. SBS to high-gold content alloy after thermocycling was 33.3 MPa by M.L. Primer. None of the primers was effective for pure Pd and high-palladium content alloy after thermocycling.