Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
Comparative Study
. 2011 Apr;39(4):309-15.
doi: 10.1016/j.jdent.2011.01.009. Epub 2011 Feb 1.

Effects of light attenuation by fibre posts on polymerization of a dual-cured resin cement and microleakage of post-restored teeth

Affiliations
Comparative Study

Effects of light attenuation by fibre posts on polymerization of a dual-cured resin cement and microleakage of post-restored teeth

Yi-Ching Ho et al. J Dent. 2011 Apr.

Abstract

Objectives: The influence of light transmitting ability of different fibre posts on the polymerization of a dual-cured resin cement, and the further microleakage of the post-restored endodontically treated teeth were examined.

Methods: An LED curing light was used as light source and the measurements of 470 nm irradiances were made at 1mm intervals along the posts (P-Lux, P-White, and P-Steel). The polymerization of a dual-cured resin cement surrounding the posts at five depths (0, 2, 5, 8, and 10mm) from the top was evaluated using micro-Raman spectra after 40s light-curing. Meanwhile, 36 human single-rooted endodontically treated teeth were randomly divided into three groups and restored with these posts and the cement according to the manufacturers' instructions. Microleakages of the post-restored teeth were compared using an electrochemical measurement system on three consecutive days, and statistically analysed using nonparametric tests.

Results: Light transmission through fibre posts was exponentially reduced as the depth increased (p<0.05, R(2)>0.95), and the polymerization of the resin cement beyond the depth of 5mm significantly declined for all specimens (p<0.05). Fibre posts displayed higher value of light transmission, exhibited a higher polymerization rate of surrounding resin cement, and also demonstrated less microleakage; whilst P-Steel posts had the lowest polymerization rate and produced higher microleakage (p<0.017).

Conclusions: The effective radiance along the post was diminished exponentially, which features the insufficient polymerization of a dual-cured resin cement surrounding the posts at apical region and might therefore influence the microleakage of post-restored teeth.