. 2011 Oct;8(4):183-8.
doi: 10.4103/1735-3327.86034.

The effect of acidulated phosphate fluoride incorporated phosphoric acid etchant on shear bond strength of orthodontic brackets

Behnam Khosravanifard  1 , Reyhaneh Yazdani, Hamid Rakhshan, Vahid Rakhshan
Affiliations

The effect of acidulated phosphate fluoride incorporated phosphoric acid etchant on shear bond strength of orthodontic brackets

Behnam Khosravanifard et al. Dent Res J (Isfahan). 2011 Oct.

Abstract

Background: The aim of this study was to evaluate the effect of adding acidulated phosphate fluoride (APF) to phosphoric acid etchant on shear bond strength (SBS) and adhesive remnant index (ARI) of orthodontic brackets bonded to etched teeth.

Methods: In this in vitro experimental study, 40 human premolars were etched with 37% phosphoric acid solution (Dentsply) blended with 0, 25%, 50%, and 75% fractions of 1.23% APF (Dentsply). The brackets (Mini Dyna Lock, 3M) were bonded (Transbond XT, 3M) and were subjected to 96 hours of 37°C incubation and thermocycling procedures (2000 cycles, 5-55°C, dwell time = 30 s). Then, they were debonded at 1-mm crosshead speed to measure the SBS. The ARI was estimated at 10× magnification. The data were analyzed using the tests one-way analysis of variance (ANOVA), Tukey, chi-square, one-sample t-test, and Spearman correlation.

Results: The SBS of the groups control, 25%, 50%, and 75% APF were 11.90±2.72, 8.01±3.13, 5.40±2.51, and 3.27±2.01 MPa, respectively. Mean ARI scores of these groups were 2.4 (control), 4.3, 4.7, and 4.8, respectively. According to the Tukey's test, only the mean SBS of the second group (25%) was not different from the control group (P=0.091).

Conclusion: Adding about 20-25% of 1.23% APF to the phosphoric acid etchant might considerably reduce the amount of residual adhesive, without compromising the SBS.

Keywords: Acidulated phosphate fluoride; dental materials; orthodontics; phosphoric acid; topical fluorides.

PubMed Disclaimer

Conflict of interest statement

Conflict of Interest: None declared.

Figures

Figure 1
Figure 1
Mounting the specimen with the bracket slot standing horizontally. The bracket is color coded with o-rings
Figure 2
Figure 2
The mean SBS (and 95% CI) of the groups (MPA)
Figure 3
Figure 3
By increasing the APF:etchant ratio, the SBS and the amount of remnant adhesive decreased. The vertical band corresponds to a range of APF ratios that can result in approximately at least 6–8 MPa SBS values
See this image and copyright information in PMC

References

    1. Kim M, Lim B, Chang W, Lee Y, Rhee S, Yang H. Phosphoric acid incorporated with acidulated phosphate fluoride gel etchant effects on bracket bonding. Angle Orthod. 2005;75:678–84. - PubMed
    1. Cacciafesta V, Sfondrini M, Calvi D, Scribante A. Effect of fluoride application on shear bond strength of brackets bonded with a resin-modified glass-ionomer. Am J Orthod Dentofac Orthop. 2005;127:580–3. - PubMed
    1. Meng C, Wang W, Yeh I. Fluoridated etching on orthodontic bonding. Am J Orthod Dentofac Orthop. 1997;112:259–62. - PubMed
    1. Khosravanifard B, Nemati-Anaraki S, Nili S, Rakhshan V. Assessing the effects of three resin removal methods and bracket sandblasting on shear bond strength of metallic orthodontic brackets and enamel surface. Orthod Waves. 2011;70:27–38.
    1. Khosravanifard B, Rakhshan V, Saadatmand A. Effects of blood and saliva contamination on shear bond strength of metal orthodontic brackets and evaluating certain methods for reversing the effect of contamination. Orthod Waves. 2010;69:156–63.

LinkOut - more resources