Direct observation of ferrielectricity at ferroelastic domain boundaries in CaTiO3 by electron microscopy

Abstract

High-resolution aberration-corrected transmission electron microscopy aided by statistical parameter estimation theory is used to quantify localized displacements at a (110) twin boundary in orthorhombic CaTiO(3). The displacements are 3-6 pm for the Ti atoms and confined to a thin layer. This is the first direct observation of the generation of ferroelectricity by interfaces inside this material which opens the door for domain boundary engineering.