Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2014 Oct;30(10):1136-46.
doi: 10.1016/j.dental.2014.07.004. Epub 2014 Aug 10.

Effect of different surface treatments on the hydrothermal degradation of a 3Y-TZP ceramic for dental implants

Affiliations

Effect of different surface treatments on the hydrothermal degradation of a 3Y-TZP ceramic for dental implants

M Cattani-Lorente et al. Dent Mater. 2014 Oct.

Abstract

Objectives: Implant surface modifications are intended to enhance bone integration. The objective of this study was to assess the effect of different surface treatments on the resistance to hydrothermal degradation, hardness and elastic modulus of a 3Y-TZP ceramic used for dental implants.

Methods: Samples grouped according to their surface morphologies (AS, as-sintered; C, coated; P, dry-polished; R, roughened; PA, polished and annealed; RA, roughened and annealed) were subjected to accelerated hydrothermal degradation (LTD) by exposure to water steam (134°C, 2bars) for 100h. The t-m phase transformation was quantified by grazing incidence X-ray diffraction (GIXDR) and by combined focused ion beam and scanning electron microscopy (FIB-SEM). Elastic modulus and hardness before- and after prolonged aging (100h) were assessed by nanoindentation.

Results: AS and C specimens presented a better resistance to hydrothermal degradation than P and R samples. After prolonged aging, the depth of the monoclinic transformed layer ranged from 11μm to 14μm. Hydrothermal degradation led to a significant decrease of elastic modulus and hardness.

Significance: Surface treatments affected the resistance to hydrothermal degradation of the 3Y-TZP ceramic. Dry mechanical surface modifications should be avoided since a high t-m transformation rate associated to the initial monoclinic content was observed. Annealing was useful to reverse the initial t-m transformation, but did not improve the resistance to hydrothermal degradation.

Keywords: 3Y-TZP ceramic; Elastic modulus; FIB-SEM; GIXRD; LTD; Nanoindentation; Surface hardness.