Effect of γ-irradiation on the physical and mechanical properties of kefiran biopolymer film

Abstract

In this study, the effect of different γ-ray dosages (3, 6, and 9 kGy) on the functional properties of kefiran biopolymer was investigated. The obtained results showed that increasing γ-ray dosage brought about an increase in the tensile strength of film specimens up to three-times. However, elongation at break, and tensile energy to break of γ-irradiated kefiran films decreased in the wake of increasing γ-ray dosage. γ-Irradiation could improve surface hydrophobicity, sensitivity of kefiran film specimens to water, and water vapor permeability, but yellowness of films increased, simultaneously. XRD spectrum confirmed increased crystallinity of γ-irradiated films. Melting point of films was constant but glass transition temperature decreased drastically at high γ-ray dosage (9 kGy). ATR-FTIR analysis confirmed that γ-ray engendered no changes in chemical functional groups. According to the result, a mechanism was proposed to percept the effects of γ-irradiation on kefiran biopolymer and its role on the functional properties of kefiran film. Hence, the functional properties of kefiran films were depend on the ratio of cross-linkages between polymer chains and produced mono and disaccharide by γ-irradiation.

Keywords: Kefiran; Mechanism; γ-Irradiation.