Research on polyvinylidene fluoride (PVDF) hollow-fiber hemodialyzer

Abstract

In this study, polyvinylidene fluoride (PVDF) hollow-fiber hemodialysis membranes were prepared by non-solvent-induced phase separation. The PVDF hollow-fiber hemodialyzers were prepared by centrifugal casting. The results showed that the PVDF membrane had better mechanical and separation properties when the membrane wall thickness was 40 μm and the N,N-dimethylacetamide in the core was 70 Vol%. Compared with commercial polysulfone hemodialysis membrane (Fresenius F60S membrane), the PVDF membrane had better mechanical property and ultrafiltration (UF) flux of pure water. The PVDF dialyzer's removal efficiency for middle molecules was proven to be much higher than that of the F60S dialyzer. The UF coefficient of a high-flux PVDF dialyzer is 62.6 ml/h/mm Hg, whereas F60S is 42.5 ml/h/mm Hg, which can promote clearance for middle molecules.