Reduced plasma-induced damage to near-surface nitrogen-vacancy centers in diamond

Abstract

Understanding plasma etch damage on near-surface nitrogen vacancy (NV) centers in diamond is essential for preserving NV emission in photonic structures and magnetometry systems. We have developed a methodology to compare the optical properties of ensemble NV centers initially 70 nm from the surface brought closer to the surface through etching with O2 plasmas in three different reactors. We employ a conventional reactive ion etcher, a barrel etcher, and a downstream etcher. We find that, irrespective of the etcher used, NV luminescence dims steadily as NVs are brought closer to the surface due to optical and surface effects. When NVs are less than 40 nm from the surface, differences in damage from the three different plasma processes affect the NV emission intensity in different ways. Diamond that is etched using the conventional etching method shows a greatly reduced NV luminescence, whereas NVs 15 nm from the surface still survive when the diamond is etched in the downstream reactor. As a result, downstream etching provides a possible alternative method for low damage etching of diamond for preservation of near surface NV properties.

Keywords: etching; nitrogen vacancy; optics; plasma damage.