Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2016 May;12(17):2376-84.
doi: 10.1002/smll.201503855. Epub 2016 Mar 8.

Creating Pores on Graphene Platelets by Low-Temperature KOH Activation for Enhanced Electrochemical Performance

Affiliations

Creating Pores on Graphene Platelets by Low-Temperature KOH Activation for Enhanced Electrochemical Performance

Shuilin Wu et al. Small. 2016 May.

Abstract

KOH activation of microwave exfoliated graphite oxide (MEGO) is investigated in detail at temperatures of 450-550 °C. Out of the activation temperature range conventionally used for the preparation of activated carbons (>600 °C), the reaction between KOH and MEGO platelets at relatively low temperatures allows one to trace the structural transition from quasi-two-dimensional graphene platelets to three-dimensional porous carbon. In addition, it is found that nanometer-sized pores are created in the graphene platelets at the activation temperature of around 450 °C, leading to a carbon that maintains the platelet-like morphology, yet with a specific surface area much higher than MEGO (e.g., increased from 156 to 937 m(2) g(-1) ). Such a porous yet highly conducting carbon shows a largely enhanced electrochemical activity and thus improved electrochemical performance when being used as electrodes in supercapacitors. A specific capacitance of 265 F g(-1) (185 F cm(-3) ) is obtained at a current density of 1 A g(-1) in 6 m KOH electrolyte, which remains 223 F g(-1) (156 F cm(-3) ) at the current density of 10 A g(-1) .

Keywords: KOH activation; graphene; platelets; supercapacitors.