Radiofrequency-activated PMMA-augmentation through cannulated pedicle screws: A cadaver study to determine the biomechanical benefits in the osteoporotic spine

Abstract

Introduction: PMMA-augmentation of pedicle screws strengthens the bone-screw-interface reducing cut-out risk. Injection of fluid cement bears a higher risk of extravasation, with difficulty of application because of inconsistent viscosity and limited injection time.

Objective: To test a new method of cement augmentation of pedicle screws using radiofrequency-activated PMMA, which is suspected to be easier to apply and have less extravasations.

Methods: Twenty-seven fresh-frozen human cadaver lumbar spines were divided into 18 osteoporotic (BMD ≤ 0.8 g/cm2) and 9 non-osteoporotic (BMD > 0.8 g/cm2) vertebral bodies. Bipedicular cannulated pedicle screws were implanted into the vertebral bodies; right screws were augmented with ultra-high viscosity PMMA, whereas un-cemented left pedicle screws served as negative controls. Cement distribution was controlled with fluoroscopy and CT scans. Axial pullout forces of the screws were measured with a material testing machine, and results were analyzed statistically.

Results: Fluoroscopy and CT scans showed that in all cases an adequately big cement depot with homogenous form and no signs of extravasation was injected. Pullout forces showed significant differences (p < 0.001) between the augmented and non-augmented pedicle screws for bone densities below 0.8 g/cm2 (661.9 N ± 439) and over 0.8 g/cm2 (744.9 N ± 415).

Conclusions: Pullout-forces were significantly increased in osteoporotic as well as in non-osteoporotic vertebral bodies without a significant difference between these groups using this standardized, simple procedure with increased control and less complications like extravasation.

Keywords: Osteoporosis; PMMA; biomechanical analysis; pedicle screw; polymethylmethacrylate; spinal fractures; spondylodesis.