Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
Randomized Controlled Trial
. 2017 Apr;32(4):1186-1191.
doi: 10.1016/j.arth.2016.10.037. Epub 2016 Nov 8.

The Relationship Between Polyethylene Wear and Periprosthetic Osteolysis in Total Hip Arthroplasty at 12 Years in a Randomized Controlled Trial Cohort

Affiliations
Randomized Controlled Trial

The Relationship Between Polyethylene Wear and Periprosthetic Osteolysis in Total Hip Arthroplasty at 12 Years in a Randomized Controlled Trial Cohort

John A J Broomfield et al. J Arthroplasty. 2017 Apr.

Abstract

Background: Polyethylene acetabular components are common in hip arthroplasty. Highly cross-linked polyethylene (HXLPE) has lower wear than ultra-high molecular weight polyethylene (UHMWPE). Evidence suggests that wear particles induce inflammation causing periprosthetic osteolysis contributing to implant loosening with wear rates of 0.05 mm/y were considered safe. We aimed to compare incidence and volume of periacetabular osteolysis between HXLPE and UHMWPE using computed tomography.

Methods: Initially, 54 hips in 53 patients were randomized to HXLPE or UHMWPE acetabular liner. At 10 years, 39 hips in 38 patients remained for the radiostereometric analysis' demonstrating significantly lower wear in the HXLPE group. At 12 years, 14 hips in 13 patients were lost to follow-up leaving 25 hips for computed tomography assessment. Images were reconstructed to detect osteolysis and where identified, areas were segmented and volumized.

Results: Osteolysis was observed in 8 patients, 7 from the UHMWPE group and only 1 from the HXLPE group (Fisher exact, P = .042). There was no correlation between the amount of polyethylene wear and osteolysis volume; however, the radiostereometric analysis-measured wear rate in patients with osteolysis from both groups was significantly higher than overall average wear rate.

Conclusion: This data demonstrates lower incidence of periacetabular osteolysis in the HXLPE group of a small cohort. Although numbers are too low to estimate causation, in the context of lower wear in the HXLPE group, this finding supports the hypothesis that HXLPE may not elevate osteolysis risk, and hence does not suggest that HXLPE wear particles are more biologically active than those generated by earlier generations of polyethylene.

Keywords: Computed Tomography; RSA; highly cross-linked polyethylene; periprosthetic osteolysis; polyethylene wear; primary total hip arthroplasty.