Boron nitride nanotubes as novel fillers for improving the properties of dental adhesives

Abstract

Objective: This study aimed to evaluate the physical-chemical properties of experimental dental adhesives containing boron nitride nanotubes (BNNTs) as inorganic fillers.

Methods: An experimental adhesive resin was prepared using HEMA-BisGMA, 66/33wt% (control). Inorganic BNNT fillers were first analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and then incorporated into the adhesive at different concentration (0.05, 0.075, 0.1, 0.15wt%). Degree of conversion (DC), ultimate strength, contact angle, surface free energy (SFE) microhardness, softening in solvent and bioactivity were assessed.

Results: Scanning and transmission electron microscopy (SEM and TEM) showed BNNTs with diameter ranging from 5 to 10nm with close end tips. No changes in DC were observed after incorporating BNNTs up to 0.15wt%. The contact angles of water and α-bromonaphthalene increased (p<0.05) and consequently the SFE decreased after incorporating BNNTs to the polymer matrix. Microhardness and solvent degradation strength increased after incorporation of 0.075, 0.1 and 0.15wt% BNNTs. Mineral deposition was found after 7days of immersion on adhesive specimens after incorporation of BNNT.

Conclusions: The incorporation of BNNTs up to 0.15wt% improved the chemical and mechanical properties of dental adhesives and promoted mineral deposition.

Clinical significance: Incorporation of boron nitride nanotubes into adhesive resin materials improved physical-chemical properties and increased mineral deposition on its surface allowing enhanced properties of the resin-dentin interface. Thus, the novel adhesive material is promising as a dental adhesive and may contribute to the stability of the dentin-resin bonding.

Keywords: Dental cement; Remineralization; Resin cement.