The effects of Biodentine/polycaprolactone three-dimensional-scaffold with odontogenesis properties on human dental pulp cells

Abstract

Aim: To determine the feasibility of using three-dimensional printed Biodentine/polycaprolactone composite scaffolds for orthopaedic and dental applications. The physicochemical properties and the odontogenic differentiation of human dental pulp cells (hDPCs) were investigated.

Methodology: Biodentine was well-suspended in ethanol and dropped slowly into molten polycaprolactone with vigorous stirring. The Biodentine/polycaprolactone composite scaffolds were then fabricated into controlled macropore sizes and structures using an extrusion-based three-dimensional (3D) printer. The mechanical properties, bioactivity, and the proliferation and odontogenic differentiation of human dental pulp cells (hDPCs) cultured on the scaffolds were evaluated.

Results: Biodentine/polycaprolactone scaffolds had uniform macropores 550 μm in size with established interconnections and a compressive strength of 6.5 MPa. In addition, the composite scaffolds exhibited a good apatite-forming ability and were capable of supporting the proliferation and differentiation of hDPCs.

Conclusion: The composite scaffolds fabricated by an extrusion-based 3D printing technique had similar characteristics to Biodentine cement, including bioactivity and the ability to promote the differentiation of hDPCs. These results indicate that the composite scaffold would be a candidate for dental and bone regeneration.

Keywords: Biodentine; human dental pulp cell; odontogenesis; polycaprolactone; three-dimensional printing.