Oxidation and Tribological Behavior of Ti-B-C-N-Si Nanocomposite Films Deposited by Pulsed Unbalanced Magnetron Sputtering

Abstract

Quinary Ti-B-C-N-Si nanocomposite films were deposited onto AISI 304 substrates using a pulsed d.c. magnetron sputtering system. The quinary Ti-B-C-N-Si (5 at.%) film showed excellent tribological and wear properties compared with those of the Ti-B-C-N films. The steady friction coefficient of 0.151 and a wear rate of 2 × 10-6 mm3N-1m-1 were measured for the Ti-B-C-N-Si films. The oxidation behavior of Ti-B-C-N-Si nanocomposite films was systematically investigated using X-ray diffraction (XRD), and thermal analyzer with differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). It is concluded that the addition of Si into the Ti-B-C-N film improved the tribological properties and oxidation resistance of the Ti-B-C-N-Si films. The improvements are due to the formation of an amorphous SiOx phase, which plays a major role in the self-lubricant tribo-layers and oxidation barrier on the film surface or in the grain boundaries, respectively.