Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2018 Jul 13;10(27):13022-13027.
doi: 10.1039/c8nr01065j.

Elastic properties and breaking strengths of GaS, GaSe and GaTe nanosheets

Affiliations

Elastic properties and breaking strengths of GaS, GaSe and GaTe nanosheets

Basant Chitara et al. Nanoscale. .

Abstract

Gallium sulphide (GaS), gallium selenide (GaSe), and gallium telluride (GaTe), belonging to the group-III monochalcogenide family, have shown promising optoelectronic performance over graphene and monolayer molybdenum disulphide (MoS2). However, to date, the mechanical properties of these materials have not been investigated, which hinders their utilisation in flexible electronics and optomechanics. Here, we characterize the elastic properties and breaking strengths of suspended two-dimensional (2D) nanosheets of GaS, GaSe, and GaTe, using atomic force microscopy. The 2D Young's modulus values of ∼10 nm thick GaS, GaSe, and GaTe were found to be 1732 ± 154 N m-1, 819 ± 127 N m-1, and 246 ± 160 N m-1, respectively, corresponding to the three-dimensional (3D) Young's modulus values of 173 ± 15 GPa, 81.9 ± 12.7 GPa, and 24.6 ± 16 GPa, respectively. The pre-tension values of these nanosheets were estimated to be 0.34 ± 0.12 N m-1, 0.14 ± 0.04 N m-1, and 0.15 ± 0.03 N m-1 for GaS, GaSe, and GaTe, respectively. GaS nanosheets exhibited the highest Young's modulus (173 GPa) among these nanosheets, which is comparable to that of WS2 and WSe2. A failure characteristic study over these group-III monochalcogenides revealed that these materials can withstand stresses of up to 8 GPa and a maximal strain of 7% before breaking. Altogether, our findings indicate that GaS, GaSe, and GaTe are attractive candidates for use in stretchable electronic applications and in future optomechanical devices.