Comprehensive characterization of silica-modified silicon rubbers

Abstract

In this study a commercially liquid silicone rubber was filled with fumed silica particles in different concentrations and evaluated for medical applications. The thermal, morphological and mechanical properties of silicone/silica composite samples were studied before and after aging, flexural tests and immersion in saline environment. Understanding the effect of silica content, aging conditions and thickness (from 0.6 to 2 mm) of the samples on the behavior of these materials in different environments is crucial for applications as implantable devices. Before inducing any mechanical stress, tensile strength was found to increase for samples containing 3 or 5 wt% of fumed silica, depending on the thickness. A similar trend was observed after 10⁶ flexes for tensile strength, storage modulus and hardness at room temperature, which increased with the concentration of fumed silica. Moreover, tensile strength decreased with increasing the thickness of the samples from 0.6 to 2 mm. The thermal degradation was found to start at higher temperature in the case of the composites as compared with neat silicone, however, the glass transition and melting temperatures were only slightly modified by the presence of the silica particles, regardless the mechanical aging. The MTT assay using L929 fibroblasts mouse cells showed a good short-time cytocompatibility for both silicone elastomer and the composite with 3 wt% fumed silica. Similarly, the measurement of the cytokine secretion revealed no inflammatory response.