Microshear Bond Strength of Scotchbond Universal Adhesive to Primary and Permanent Dentin: A Six-Month in Vitro Study

Abstract

Objectives: This study aimed to assess the microshear bond strength (MSBS) of Scotchbond Universal adhesive, used in self-etch and etch-and-rinse modes, to primary and permanent dentin at 24 hours and six months.

Materials and methods: A total of 88 composite micro-cylinders were divided into eight groups (n=11) as follows: (A) Etch-and-rinse, 24 hours, primary dentin; (B) Self-etch, 24 hours, primary dentin; (C) Etch-and-rinse, six months, primary dentin; (D) Self-etch, six months, primary dentin; (E) Etch-and-rinse, 24 hours, permanent dentin; (F) Self-etch, 24 hours, permanent dentin; (G) Etch-and-rinse, six months, permanent dentin; (H) Self-etch, six months, permanent dentin. The MSBS was measured by a testing machine at a crosshead speed of 0.5 mm/minute. Data were analyzed using three-way analysis of variance (ANOVA).

Results: The mean MSBS was 12.3±2.3 MPa in A, 18.8±4.1 MPa in B, 11.9±3.7 MPa in C, 16±2.9 MPa in D, 19.1±2.7 MPa in E, 22.8±4.1 MPa in F, 16.2±2.6 MPa in G, and 17.2±4.4 MPa in H. In the self-etch mode, the MSBS was significantly higher than that in the etch-and-rinse mode (P<0.001). The MSBS in permanent teeth was significantly higher than primary teeth (P<0.001). At six months, the MSBS significantly decreased in all groups (P<0.001).

Conclusion: The micro-shear bond strength of Scotchbond Universal adhesive decreases over time and depends on the type of tooth and the mode of application of the adhesive.

Keywords: Dentin Bonding Agents; Scotchbond; Shear Strength.