Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2021 Nov;126(5):698-702.
doi: 10.1016/j.prosdent.2020.08.016. Epub 2020 Oct 27.

Effect of surface treatment and cleaning on the bond strength to polymer-infiltrated ceramic network CAD-CAM material

Julian Conejo  1 , Fusun Ozer  2 , Francis Mante  3 , Pablo J Atria  4 , Markus B Blatz  5
Affiliations

Effect of surface treatment and cleaning on the bond strength to polymer-infiltrated ceramic network CAD-CAM material

Julian Conejo et al. J Prosthet Dent. 2021 Nov.

Abstract

Statement of problem: Optimal composite resin bonds to polymer-infiltrated ceramic network (PICN) computer-aided design and computer-aided manufacturing (CAD-CAM) materials are essential for clinical success. However, comparative bond strength studies on the influence of different etching and cleaning methods on these materials are lacking.

Purpose: The purpose of this in vitro study was to measure and compare the microshear bond strength (μSBS) of a composite resin cement with that of a PICN material after different surface treatment and cleaning methods.

Material and methods: Seventy specimens of a CAD-CAM PICN were divided into 7 groups (n=10): no treatment (control), hydrofluoric acid etching for 20 seconds (HF20), 60 seconds (HF60), 120 seconds (HF120), HF20 + phosphoric acid for 60 seconds and ultrasonic bath for 5 minutes, HF60 + PH, and HF120 + PH. After surface treatment, a silane coupling agent and composite resin cement were applied. Microshear bond strength was determined, and data were analyzed with 1-way ANOVA and Tukey post hoc multiple comparison tests (α=.05).

Results: All HF acid treatments resulted in a significant increase in bond strength to the polymer-infiltrated ceramic network material (P=.02). Bond strength values for HF etching for 20 seconds were significantly lower than those for 60 seconds and 120 seconds (P=.034). No difference was found between 60 seconds and 120 seconds of HF etching time (P=.986). Additional surface treatment with phosphoric acid 60 seconds and ultrasonic bath 5 minutes did not improve the bond strength beyond values obtained by hydrofluoric acid treatment only (P=.834). Most failures were cohesive.

Conclusions: Acid etching and surface treatment have significant effects on composite resin bond strength to a PICN CAD-CAM material. HF etching for 60 seconds or 120 seconds provides the highest bond strengths. Cleaning methods after etching did not have any significant effect on bond strength.