Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2021 Jun:202:111699.
doi: 10.1016/j.colsurfb.2021.111699. Epub 2021 Mar 15.

Electrosprayed calcium silicate nanoparticle-coated titanium implant with improved antibacterial activity and osteogenesis

Affiliations

Electrosprayed calcium silicate nanoparticle-coated titanium implant with improved antibacterial activity and osteogenesis

Csaba Buga et al. Colloids Surf B Biointerfaces. 2021 Jun.

Abstract

To ensure clinical success, the implant and the surrounding bone tissue must not only be integrated, but also must not be suspected of infection. In this work, an antibacterial and bioactive nanostructured calcium silicate (CaSi) layer on titanium substrate by an electrospray deposition method was prepared, followed by annealing at 700, 750 and 800 °C to improve the bonding strength of the CaSi coating. The phase composition, microstructure and bonding strength of the CaSi coatings were examined. Human mesenchymal stem cells (hMSCs), Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) species were used to analyze the osteogenic and antibacterial activity of the coatings, respectively. Experimental results showed that the as-prepared CaSi coating was mainly composted of β-dicalcium silicate phase with a particle size of about 300 nm. After annealing, the thickness of the oxidation reaction layer increased obviously from 0.3 μm to 1 μm with increase in temperature, which was confirmed by the cross-sectional morphology and element depth profile. The bonding strength of the coating annealed at 750 °C (19.0 MPa) was significantly higher (p < 0.05) than that of the as-prepared coating (4.4 MPa) and the ISO 13,779 standard (15 MPa). The results of antibacterial efficacy and stem cell osteogenesis consistently elaborated that the 750 °C-annealed coating had higher activity than the as-prepared coating and the Ti control. It is concluded that after annealing at 750 °C, the CaSi nanoparticle-coated Ti implant had good bond strength, osteogenic and antibacterial activity.

Keywords: Antibacterial coating; Bioactive coating; Bonding strength; Calcium silicate; Electrospray deposition.