Novel CAD-CAM zirconia coping design to enhance the aesthetics and strength for anterior PLZ crowns

Abstract

Background: The aesthetics and strength of anterior porcelain layered zirconia (PLZ) crowns are mainly affected by the zirconia (Zr) coping design. There is a need for a modified design to enhance aesthetics with strength.

Objectives: The purpose of this study was to compare the fracture resistance of anterior PLZ crowns having modified CAD-CAM Zr coping designs (in terms of thickness and marginal collar designs) with standard Zr copings.

Methods: Fifty PLZ crowns were fabricated and divided into two groups: Gr 1: Standard Zr Coping (SZC) (control gr) with 0.5 mm thickness (Facial-F, Mesial-M, Distal-D, incisal-I, and Palatal-P) without a collar; Gr 2: Collar Zr Coping (CZC) (test gr) with 2.5 mm collar height on M, D, P and 0.2 mm F and variable facial wall thickness. Subgroups: Gr 2a: (CZC-0.5 mm) facial wall thickness 0.5 mm; Gr 2b: (CZC-0.4 mm) facial wall thickness 0.4 mm; Gr 2c: (CZC-0.3 mm) facial wall thickness 0.3 mm; Gr 2d: (CZC-0.2 mm) facial wall thickness 0.2 mm. The fracture load was determined and analysed using One-way ANOVA and Dunnet test.

Results: The minimum fracture load was 927.36 ± 127.80 N observed for Gr 2c (CZC at 0.3 mm) while the maximum fracture load was 1373.61 ± 146.54 N observed for Gr 2a (CZC at 0.5 mm). A highly significant difference in mean fracture load among various Zr coping groups (p< 0.001) was determined.

Conclusions: Novel Zr coping design for anterior PLZ crowns can provide better aesthetics with strength. Reducing the thickness of Zr coping in the aesthetic zone to 0.2 mm and providing a modified collar design (2.5 mm collar height on M, D, P, and 0.2 mm F) would provide strength without jeopardizing aesthetics.

Keywords: Zirconia; ceramic veneering; chipping; compressive load; copings design; fracture strength; marginal collar height.