Conductive polypyrrole-encapsulated silk fibroin fibers for cardiac tissue engineering

Abstract

Polypyrrole (PPy) has been utilized in smart scaffolds to improve the functionality of the engineered cardiac tissue. Compared to the commonly used aqueous coating, here, PPy was blended into silk fibroin (SF) solution to electrospin conductive PPy-encapsulated SF nanofibers. Combinations of various SF concentrations (5%, 7%, and 12%) and different PPy-to-SF ratios (15:85, 30:70, and 40:60) were compared. PPy reduced the fiber diameter (0.431 ± 0.060 μm), better-mimicking the myocardium fibrils. Conductive mats with 7% SF showed the closest mechanical properties (1.437 ± 0.044 MPa) to the native myocardium; meanwhile, a PPy-to-SF ratio of 15:85 exhibited sufficient electrical conductivity for cardiomyocytes (CMs). In vitro studies using three different types of CM demonstrated that the hybrid mats support CM contraction. Primary neonatal rat CMs on the mat with a PPy-to-SF ratio of 15:85 were elongated and orientated anisotropically with locally organized sarcomeric striations. By contrast, human-induced pluripotent stem cell derived-CMs on the mat with a PPy-to-SF ratio of 30:70 exhibited the strongest contractions. Contraction synchrony was further improved by external stimulation. Taken together, these findings indicated the great potential of the PPy-encapsulated SF electrospun mat for cardiac tissue engineering.

Keywords: Cardiac patch; Conductive biomaterials; Electrospinning; Polypyrrole; Silk fibroin.