Skip to main page content
U.S. flag

An official website of the United States government

Dot gov

The .gov means it’s official.
Federal government websites often end in .gov or .mil. Before sharing sensitive information, make sure you’re on a federal government site.

Https

The site is secure.
The https:// ensures that you are connecting to the official website and that any information you provide is encrypted and transmitted securely.

Access keys NCBI Homepage MyNCBI Homepage Main Content Main Navigation
. 2022 Nov 14;61(46):e202211172.
doi: 10.1002/anie.202211172. Epub 2022 Oct 17.

Narrowband Emissive TADF Conjugated Polymers towards Highly Efficient Solution-Processible OLEDs

Tao Wang  1   2 , Yang Zou  1 , Zhongyan Huang  1 , Nengquan Li  1 , Jingsheng Miao  1 , Chuluo Yang  1
Affiliations

Narrowband Emissive TADF Conjugated Polymers towards Highly Efficient Solution-Processible OLEDs

Tao Wang et al. Angew Chem Int Ed Engl. .

Abstract

Thermally activated delayed fluorescence (TADF) conjugated polymers usually show broad emission spectra due to the large structure relaxation, which is not desirable for high-quality organic light-emitting diode (OLED) displays. Herein, through attaching multiple resonance (MR) induced emitting moiety as pendant onto the polycarbazole backbone, TADF conjugated polymers with narrowband emission are demonstrated. The obtained conjugated polymers exhibit typical TADF characteristics with narrowband emission with full-width at half-maximums (FWHMs) of 33-43 nm. The solution-processed devices employing these polymers as emissive layers realize excellent performances with maximum external quantum efficiency (EQE) of 17.5 %, emission peak at 496 nm and FWHM of 34 nm.

Keywords: Conjugated Polymer; Multiple Resonance; Narrowband Emission; Organic Light-Emitting Diode; Thermally Activated Delayed Fluorescence.

PubMed Disclaimer

References

    1. Q. Wei, Z. Ge, B. Voit, Macromol. Rapid Commun. 2019, 40, 1800570.
    1. B. Zhang, Y. Cheng, Chem. Rec. 2019, 19, 1624-1643.
    1. T. Huang, W. Jiang, L. Duan, J. Mater. Chem. C 2018, 6, 5577-5596.
    1. T. Jiang, Y. Liu, Z. Ren, S. Yan, Polym. Chem. 2020, 11, 1555-1571.
    1. J. Rao, X. Liu, X. Li, L. Yang, L. Zhao, S. Wang, J. Ding, L. Wang, Angew. Chem. Int. Ed. 2020, 59, 1320-1326;

LinkOut - more resources