Tuning the physiochemical properties of polycaprolactone-hydroxyapatite composite films by gamma irradiation for biomedical applications

Abstract

Physiochemical properties of polycaprolactone-hydroxyapatite (PCL-HAp) composites were investigated in the pristine and after irradiation of γ rays (25, 50, 75, and 100 kGy). PCL-HAp composites were synthesized by solvent evaporation and characterized using spectroscopic methods as well as biological assays. The surface roughness (RMS) of the irradiated composite film (at 75 kGy) was 80 times higher than that of the pristine. Irradiation tailors the contact angle of the films from 77° to 90° (at 100 kGy). A decrease in particle size (at 100 kGy) of HAp nanorods in PCL-HAp composites film was observed. The XRD peak of PCL was slightly shifted from 21.2° to 21.7° (at 100 kGy) with the decrease in crystallite size. The peak intensity of the PCL and HAp altered on irradiation that was confirmed by FTIR and Raman analysis. Further, the bandgap of the irradiated film was lowered by 13 % (at 25 kGy). The luminescence intensity decreased due to the non-radiative process induced by the irradiation defects. All the samples possess hemocompatibility percentage of <10 % as per ASTM standards. At 75 kGy, fibroblast cell proliferation was higher than the pristine and other doses. The gamma-irradiated PCL-HAp composite films are potential candidates for tissue engineering applications.

Keywords: Biopolymer composite film; Gamma irradiation; Hydroxyapatite; Polycaprolactone; TEM; Tissue engineering application.