Physicochemical properties of calcium silicate cement based endodontic sealers

Abstract

Aim: To mensure the physicochemical properties of three ceramic cement endodontic sealers AH Plus Bioceramic, Bio-C Sealer and Bio-C Sealer Ion⁺ with an epoxy resin sealer, AH Plus.

Material and methods: These properties were measured: hardening time (HT), dimensional change (DC), solubility (SL), flow (FL) and radiopacity (RD). The distilled water obtained from the SL test was analyzed with atomic absorption spectrometry. A sample calculation was made considering n = 5 repetitions for each experimental sealer evaluated. Statistical analysis was performed using one-way ANOVA and post hoc Tukey tests (p < 0.05).

Results: For the HT, AH Plus (484 ± 2.76 min) and AH Plus Bioceramic (424 ± 1.23 min) set more slowly than of Bio-C Sealer (370 ± 4.50 min) and Bio-C Sealer Ion⁺ (380 ± 1.42 min) (p < 0.05). AH Plus Bioceramic (12.56 ± 2.71 %) was more soluble than Bio-C Sealer (6.69 ± 1.67 %), Bio-C Sealer Ion⁺ (5.67 ± 2.16 %) and AH Plus (0.15 ± 0.01 %) (p < 0.05). AH Plus (0.03 ± 0.01 %) had slight expansion while the cement-based sealers had shrinkage: AH Plus Bioceramic (-1.60 ± 0.63 %) and Bio-C Sealer (-1.38 ± 0.69 %), Bio-C Sealer Ion⁺ (-5.19 ± 1.23 %) (p < 0.05). Bio-C Sealer Ion⁺ (59.80 ± 0.86 mm) and Bio-C Sealer (58.60 ± 0.98 mm) had the highest flow compared with AH Plus (56.90 ± 0.56 mm) and AH Plus Bioceramic (49.50 ± 0.63 mm) (p < 0.05). AH Plus (9.17 ± 0.06 mmAl) and AH Plus Bioceramic (8.27 ± 0.84 mmAl) showed radiopacity values when compared with those of Bio-C Sealer (4.90 ± 0.08 mmAl) and Bio-C Sealer Ion⁺ (4.14 ± 0.05 mmAl) (p > 0.05).

Conclusion: Ion release is inhered to these cement-based sealers and this result in calcium ion release.

Keywords: Calcium silicate; Endodontic; Root canal obturation; Solubility.