Influence of Thickness on the Translucency Parameter and Whiteness Index of Single-Shade Resin Composites

Abstract

The study aimed to evaluate the effect of thickness on the translucency parameter (TP) and whiteness index for dentistry (WID) of single-shade resin composites compared with a multi-shade resin composite after thermocycling. A total of 100 resin composite samples of five brands (Filtek Z250, Omnichroma, Vittra APS Unique, Zenchroma, and Charisma Diamond One) with thicknesses of 2 mm and 4 mm were prepared (n=10). CIE L*a*b* coordinates were obtained using a spectrophotometer. The resin composite samples were subjected to 10,000 thermocycles. Before and after thermocycling, TP values were calculated with the CIEDE2000 formula, and whiteness values were calculated using the WID. The influence of thickness, resin composite, and aging on these variables was analyzed using the generalized linear model (p<0.05). Omnichroma and Filtek Z250 exhibited, respectively, the highest and the lowest TP00 values compared with the other resin materials (p<0.001). The TP00 values of Zenchroma and Diamond One were similar (p>0.05). Vittra APS Unique had a lower TP than Zenchroma and Diamond One (p<0.001). Before thermocycling, the highest WID showed the combination of Vittra APS Unique with thicknesses of 2 mm (48.33±1.18). After thermocycling, the highest WID was shown in the combination of Vittra APS Unique with thicknesses of 2 mm (45.33±0.55) and 4 mm (46.23±0.94) (p<0.001). After thermocycling, the lowest WID was for the combination of Filtek Z250 with thicknesses 2 mm (21.16±0.93) and 4 mm (20.70±0.91) (p<0.001). The TP and WID values of the resin composites varied across different composites and thicknesses. Single-shade resin composites of different thicknesses demonstrated higher translucency and whiteness values than multi-shade resin composite, both before and after thermocycling.