Sodium alginate/polyvinyl alcohol semi-interpenetrating hydrogels reinforced with PEG-grafted-graphene oxide

Abstract

Semi-interpenetrating polymer network (SIPN) hydrogels composed of sodium alginate/poly (vinyl alcohol), reinforced by PEG-grafted-graphene oxide (GO-g-PEG) were prepared by ionic crosslinking of sodium alginate. The impact of grafted PEG molecular weight with two molecular weights, i.e. 400 and 2000 g/mol, and component composition were studied on the morphology, swelling behavior, mechanical and dynamic properties. SEM observation showed fine dispersion and distribution of GO-g-PEG throughout the hydrogel indicating a good interaction of particles with the components. Our results revealed that although incorporating GO-g-PEG increases the water content, it significantly enhances the mechanical properties, i.e. tensile modulus, elongation at break, and fracture toughness with a more pronounced impact at higher PEG molecular weight. As a result, the tensile modulus and the elongation at break increased by 270 % and 28 %, respectively. The SA/PVA SIPN hydrogels reinforced with the GO-g-PEG exhibit a non-linear elastic behavior with a toe at low strains. This behavior is attributed to the unique structural features of SIPN hydrogels and the orientation of GO-g-PEG particles with proper interaction with the components. The small amplitude oscillatory shear was also performed to further study the impact of SA, PVA, and GO-g-PEG compositions on the microstructure of hydrogels.

Keywords: Graphene oxide; Hydrogel; Polyvinyl alcohol; Semi-IPN; Surface modification.